by Dr. Ning-Cheng Lee
Spheres are manufactured via sequential flow/quench or reflow processes, then followed by degreasing and classification. Surface contamination or mis-handling can aggravate sphere solderability. Sphere attachment onto BGA typically is achieved via vacuum-transfer or gravity-dispensing processes, and the spheres are held in place by flux or solder paste before reflow. Welding process also in use. Bumping can be achieved via confined solder paste during reflow. Bumping with Sn62/Sn63 spheres & paste yields excellent results. Bumping with Sn62/Sn63 spheres & flux desires high viscosity, high volatility, large pitch, low print thickness, low flux activity, & small pads. Bumping with Sn10 sphere & paste exhibits no missing, and the yield increases with decreasing print thickness, decreasing volatility, increasing sphere solderability, increasing flux activity, increasing pad size, increasing metal load, & increasing pad solderability. The yield is not affected by viscosity, pitch, and reflow profile. For bumping with paste alone approach, easily releasable paste is crucial for regular print-release-reflow process. Bumping with integrated preform is promising. Reducing the thickness & width of solder links is essential for better yield.
solder, sphere, ball, BGA, Bumping, attachment, flux, solder paste, pb-free, lead-free
[Permanent Link to this Paper ]
Posted on 1 Jan 2009