It is no secret that automotive semiconductor customers are becoming increasingly demanding. The “under the hood / bonnet” electronics environment is arguably one of the most thermally

NanoFoil®requires a threshold of energy to activate. What happens if that energy value is not met?: Interdiffusion and inhibition of the NanoBond® reaction. This can happen if NanoFoil®

Many surface finishes are solderable with the right flux. Many of our electronic devices use solder to bond copper, silver, gold, and other metals, but did you know that you can solder wooden

Being the Indium Corporation, we know what indium is, where it comes from, and how to use it. But sometimes we forget that not everyone is as immersed in indium as we are. So what is indium? Of

Folks, In the category of interesting requests, Ron, a gold worker, from Guyana, sent me the following note: Dr. Ron, My colleagues use a “wet” gold technique to measure gold alloy

There are many sputtering target materials that are tricky to solder to. For those alloys we ‘bring out the big guns’ – in this case, our ultrasonic soldering

In order to NanoBond® parts that are made out of copper, nickel, or platinum, we must first apply solder to the bonding surface. This is most commonly done by melting solder directly onto the

Folks, Our discussion of Weibull Analysis continues…..Let’s say you have worked hard and assembled some SMT lead-free PCBs for thermal cycle testing. You used the best lead-free solder paste,

Sometimes one piece of NanoFoil® just isn’t enough… We often NanoBond® sputtering targets which are large enough to require multiple sheets of NanoFoil® to cover the width or

Hand cutting is only one option for shaping NanoFoil®, however it is quick, easy, and inexpensive. All you need to cut NanoFoil® with this method is a good cutting surface, metal straight

Folks, In continuing our discussion on Weibull Analysis, let’s assume we assembled some SMT and through-hole PCBs with lead-free solder paste. On this board are also some bottom-side terminated

A few years back, Indium Corporation's own Eric Bastow set up a prototype NanoFoil® plating process to demonstrate the material and cost savings of setting up a small plating bath. One of the

One question that I often hear from customers is; “Once out of the refrigerator, how long do I have to wait to allow my solder paste and/or flux to reach room temperature in order to use

はんだペーストの "グレーピング "欠陥についてはよく耳にしますが、同じような酸化の問題は他のはんだ形状でも発生します。

Tin-coated NanoFoil® is not one, but two very different products, combined. It is a heat source and a form of solder. In the world of interconnection, this is quite unique. (Shown in the picture

Folks, Let’s see how Pete is handling the wave solder crisis. Pete had to admit that he was surprised by the positive outcome of his meeting with Fred Castle. He had sent Patty a text the day

NanoFoil® is described as “reactive multilayer foil”. It is comprised of many alternating layers of aluminum and nickel which are each only nanometers thick. These layers are waiting in close

Folks, It's been a while. Let's look in on Patty…… Patty stared, bleary eyed, at her laptop screen. It was the day after the election. She and Rob were following the election